Aluminosilicate glass original sheet for Electronic Appliance Display Cover Glass with Ar/AG Coating
Ultra Clear super white Medium Alumino-Silicate electronic float glass original pieces(CHIYAN-M2) is an eco-friendly ultra-thin alumino-silicate glass with certain strength.
Usages:
1. Consumer Electronics (smart watch, smart bracelet, mobile phone, tablet, glass cover, mobile phone camera cover, PSP game console cover, etc.)
2. Industrial CNC (various equipment digital display panel glass screen covers.)
3. Home appliances (various glass appliance covers, such as air-conditioning touch panels, switch panels, electronic clock panels, etc.)
Features:
High Impact Resistance
High Scratch Resistance
High Flexibility
High Bending Strength Resistance
Applications:
• Ideal protective cover for electronic displays in:
- Smartphones
- Laptop and tablet computer screens
- Mobile devices
• Touchscreen devices
• Optical components
• High strength glass articles
Regular Thickness:
2.0mm 1.80mm 1.50mm 1.30mm
1.10mm 0.70mm 0.55mm
0.40mm 0.33mm 0.25mm
CHIYAN-M2’s 0.25~2.0mm thickness medium alumino-silicate glass has already been used in the market to meet a wide range of customers needs.
Standard Size:1300*1100mm (5th Generation)
Note: The size can be customized according to customer's needs.
Product Composition
Ultra Clear Medium Alumino-Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.
Composition items | SiO₂ | Al₂O₃ | Fe₂O₃ | CaO | MgO | K₂O | Na₂O |
Range of set value | 69.0-72.0 | 4.5-8.0 | ＜0.01 | 6.0-8.0 | 3.5-5.0 | 0.1-1.0 | 13.0-14.5 |
Chemical Tempering Process Parameter Setting Reference
Technological Parameter | 400°C | 410°C | 420°C | 430°C | ||||
CS(MPa) | DOL(um) | CS(MPa) | DOL(um) | CS(MPa) | DOL(um) | CS(MPa) | DOL(um) | |
3H | ≥650 | ≥7.0 | ≥650 | ≥8.0 | ≥650 | ≥9.0 | ≥650 | ≥10.5 |
4H | ≥600 | ≥8.0 | ≥600 | ≥9.0 | ≥600 | ≥11.0 | ≥600 | ≥12.5 |
5H | ≥600 | ≥9.0 | ≥600 | ≥10.0 | ≥600 | ≥11.5 | ≥600 | ≥13.0 |
Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.
Dimensions
NO. | Item | Specification | Detection Method |
1 | Dimensional Tolerance | 1300*1100*(±2mm) | Tape Measure |
2 | Thickness | 0.50~1.1 ±0.05m 1.3~2.0 ±0.05m | Micrometer |
3 | Thickness Difference | ≤0.04mm | Micrometer |
4 | The Diagonal Difference | ≤0.3% | Tape Measure
|
5 | Stripe | ≤Level2 | Point Sources of Light |
6 | Flatness (Before Tempering) | 0.50~0.55 ≤0.15%(=h/L) 0.70~2.0 ≤0.10%(=h/L) |
|
Appearance Specifications
NO. | Item | Specification | Detection Method | |
1 | Effective Mass Area | All areas outside 10mm of the edge are effective mass areas. |
| |
2 | Appearance Defects | Scratches | w≤0.03mm, Allowed 0.03mm＜w≤0.05mm,L≤25mm (Controlled by point defects) w＞0.05mm, Not allowed |
Fluorescent Lamp 2000-2500Lux
|
Bubbles | d≤0.05mm, Not counted 0.05mm＜d≤0.2mm, Numbers≤5 /m² d＞0.2mm,Not allowed | |||
Inclusions such as stones and sticky tin | d≤0.05mm, Not counted 0.05mm＜d≤0.2mm, Numbers≤5 /m² d＞0.2mm,Not allowed | |||
3 | Edge Defects | Chipping | Single chipping L≤2.0mm,W≤1.0mm,D≤1/2 of the thickness (as the right picture showed). The cumulative length of chipping is less than 10% of the edge length of the glass plate. |
|
4 | Cracks and missing corners | Not allowed | ||
5 | Surface stains (glass shavings, attachments, point contamination) | No stains that cannot be removed by ordinary detergents are allowed. | ||
d≤0.05mm, Not counted 0.05mm＜d≤0.3mm, Numbers≤5 /m² d＞0.3mm,Not allowed | The same method as appearance detection. | |||
Packing Quantity
S/N | L*W*T(mm) | Packing Quantity (Pieces/Box) |
1 | 1300x1100x0.25 | 900 |
2 | 1300x1100x0.33 | 1020 |
3 | 1300x1100x0.40 | 900 |
4 | 1300x1100x0.50 | 750 |
5 | 1300x1100x0.55 | 680 |
6 | 1300x1100x0.70 | 550 |
7 | 1300x1100x0.82 | 490 |
8 | 1300x1100x0.95 | 420 |
9 | 1300x1100x1.0 | 410 |
10 | 1300x1100x1.1 | 370 |
11 | 1300x1100x1.3 | 310 |
12 | 1300x1100x1.5 | 280 |
13 | 1300x1100x1.6 | 250 |
14 | 1300x1100x1.8 | 230 |
15 | 1300x1100x2.0 | 200 |
Packaging Diagram
Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed:
Storage
Storage conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.