Aluminosilicate original Glass sheet for Automotive Vehicles Windshield Laminated Safety Glass
High Alumino-Silicate original float Glass sheet(CHIYAN-H1) is an high aluminosilicate ultra-thin glass eco-friendly , which increases the Al₂O₃ contents in the ingredients to improve the ion exchange efficiency, so that it has excellent mechanical properties after chemical strengthening.
According to the melting point of the intermediate film, it can be divided into: low temperature laminated glass, high temperature laminated glass, insulating glass. According to the different materials sandwiched in the middle, it can be divided into: sandwiched paper, sandwiched cloth, sandwiched plants, sandwiched silk, sandwiched wire and many other types.
Features:
High Transmittance
High Bending Strength Resistance
Ultra Clear White
High chemical resistance
High Flexibility
High Impact Resistance
High Scratch Resistance
Conventional Thickness:
0.3mm~6mm
CHIYAN-H1’s 0.3~6.0mm thickness high alumino-silicate glass has already been used in the market to comply with a wide range of customers needs.
Standard Size:1300*1100mm (5th Generation)
Note: The size can be customized according to customer's needs.
Product Composition
High Alumino-Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.
Chemical Tempering Process Parameter
| CS | >900Mpa |
| DOL | >50um |
| 4PB | >800Mpa |
Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.
Application: Widely used in high-end smartphone, tablet pc, electronic devices screen protection, car-mounted display screen, industrial touch panels, smart home screen display fields etc.,
Packaging Diagram
High Alumino-Silicate Glass(CHIYAN-H1) is adopted Float Glass Process.
Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed:
Storage
Storage conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.